Silane
crosslinkable compounds for the manufacture of
flexible Heatshrinkable and flame retardant polyolefin
tubing.
SX716:CM401
Silane crosslinkable polyethylene compound for heat shrinkable wrap-around applications.
Special Characteristics
A silane crosslinkable polyethylene compound which has been developed for Telecom wrap-around heat shrinkable applications. The graft component SX716 is mixed with a crosslinking catalyst masterbatch CM401 generally in the ratio 95:5.
Density
g/cm²
Tensile Strength
N/mm²
Elongation %
General Notes
View Datasheet
0.92
18
450
SX736:CM424
Silane
crosslinkable compound for the production
of flexible heat shrinkable and flame
retardant polyolefin tubing.
Special
Characteristics
Material SX736 is a silane grafted compound,
curable by exposure to moist conditions,
designed specifically for the production,
by extrusion, of flexible flame retardant
heat shrinkable tubing. The graft component
SX736 is mixed with a crosslinking catalyst
masterbatch CM424 generally in the ratio
95:5. The two component system SX736:CM424
combines ease of processing with the
ability to achieve a degree of crosslinking
compatible with good expansion and contraction.
Density
g/cm²
Tensile
Strength
N/mm²
Elongation %
General
Notes
View Datasheet
1.26
13
450
For UL224 applications
SX725:CM424
Silane
crosslinkable compound for the production
of flexible heat shrinkable polyolefin
tubing.
Special
Characteristics
Material SX725 is a silane grafted compound,
curable by exposure to moist conditions,
designed specifically for the production,
by extrusion, of flexible heat shrinkable
tubing. The graft component SX725 is
mixed with a crosslinking catalyst masterbatch
CM424 generally in the ratio 95:5. The
two component system SX725:CM424 combines
ease of processing with the ability
to achieve a degree of crosslinking
compatible with good expansion and contraction.
Density
g/cm²
Tensile
Strength
N/mm²
Elongation %
General
Notes
View Datasheet
0.930
15
400
Where transparency
is required
SX738:CM424 & SX738:CM401
Silane Crosslinkable low-smoke low-toxicity halogen-free flame retardant compound for the production of Flexible Heat Shrinkable Tubing.
Special
Characteristics
SX738 is a low smoke, low fume, fire retardant silane grafted compound, curable by exposure to moist conditions, designed specifically for the production, by extrusion, of flame retardant halogen free heat shrinkable tubing. The graft component SX738 is mixed with a crosslinking catalyst masterbatch CM424 or CM401 generally in the ratio 95:5.
The two component system SX738:CM424/401 combines ease of processing with the ability to achieve a degree of crosslinking compatible with good expansion and contraction.
Density
g/cm²
Tensile Strength
N/mm²
Elongation %
General Notes
View Datasheet
1.17
11
250
Resistant to electrical tracking
SX737:CM424
Silane crosslinkable Anti-Track Compound for the production of flexible Heat Shrinkable Polyolefin Tubing.
Special Characteristics
Material SX737 is a silane grafted anti-track compound, curable by exposure to moist conditions, designed specifically for the production, by extrusion, of flexible heat shrinkable tubing for cable jointing applications. The graft component SX737 is mixed with a crosslinking catalyst masterbatch CM424 generally in the ratio 95:5.
The two component system SX737:CM424 combines ease of processing with the ability to achieve a degree of crosslinking compatible with good expansion and contraction.